|
Liquidmetal and Vitreloy are commercial names of a series of amorphous metal alloys developed by a California Institute of Technology (Caltech) research team and marketed by Liquidmetal Technologies. Liquidmetal alloys combine a number of desirable material features, including high tensile strength, excellent corrosion resistance, very high coefficient of restitution and excellent anti-wearing characteristics, while also being able to be heat-formed in processes similar to thermoplastics. Despite the name, they are not liquid at room temperature.〔liquidmetal.com. (Liquidmetal Coatings Material ). Retrieved 2008-10-23 〕 Liquidmetal was introduced for commercial applications in 2003.〔Herrman, J. (2010, August 17). Giz Explains: What Is Liquidmetal? Retrieved July 7, 2015.〕 It is used for, among other things, golf clubs, watches and covers of cell phones. The alloy was the end result of a research program into amorphous metals carried out at Caltech. It was the first of a series of experimental alloys that could achieve an amorphous structure at relatively slow cooling rates. Amorphous metals had been made before, but only in small batches because cooling rates needed to be in the millions of degrees per second. For example, amorphous wires could be fabricated by splat quenching a stream of molten metal on a spinning disk. Because Vitreloy allowed such slow cooling rates, production of larger batch sizes was possible. More recently, a number of additional alloys have been added to the Liquidmetal portfolio. These alloys also retain their amorphous structure after repeated re-heating, allowing them to be used in a wide variety of traditional machining processes. ==Characteristics== Liquidmetal alloys contain atoms of significantly different sizes. They form a dense mix with low free volume. Unlike crystalline metals, there is no obvious melting point at which viscosity drops suddenly. Vitreloy behaves more like other glasses, in that its viscosity drops gradually with increased temperature. At high temperature, it behaves in a plastic manner, allowing the mechanical properties to be controlled relatively easily during casting. The viscosity prevents the atoms moving enough to form an ordered lattice, so the material retains its amorphous properties even after being heat-formed. The alloys have relatively low softening temperatures, allowing casting of complicated shapes without need for finishing. The material properties immediately after casting are much better than those of conventional metals; usually, cast metals have worse properties than forged or wrought ones. The alloys are also malleable at low temperatures ( for the earliest formulation), and can be molded. The low free volume also results in low shrinkage during cooling. For all of these reasons, Liquidmetal can be formed into complex shapes using processes similar to thermoplastics,〔(Liquid metal behaves like plastic ), Manufacturing Engineering, March 2003 〕 which makes Liquidmetal a potential replacement for many applications where plastics would normally be used. Due to their non-crystalline (amorphous) structures, Liquidmetals are harder than alloys of titanium or aluminum of similar composition. The zirconium and titanium based Liquidmetal alloys achieved yield strength of over 1723 MPa, nearly twice the strength of conventional crystalline titanium alloys (Ti6Al4V is ~830 MPa), and about the strength of high-strength steels and some highly engineered bulk composite materials (see tensile strength for a list of common materials). However, the early casting methods introduced microscopic flaws that were excellent sites for crack propagation which led to Vitreloy being fragile like glass. Although strong, these early batches shattered easily when struck. Newer casting methods, adjustments of the alloy mixtures and other changes have improved this. The lack of grain boundaries contribute to the high yield strength (and thereby resilience) exhibited. In a demonstration, a ball bearing dropped on amorphous steel bounced significantly longer than the same bearing dropped on crystalline steel. The lack of grain boundaries in a metallic glass eliminates grain-boundary corrosion — a common problem in high-strength alloys produced by precipitation hardening and sensitized stainless steels. Liquidmetal alloys are therefore generally more corrosion resistant, both due to the mechanical structure as well as the elements used in its alloy. The combination of mechanical hardness, high elasticity and corrosion resistance makes Liquidmetal wear resistant. Although at high temperatures, plastic deformation occurs easily, almost none occurs at room temperature before the onset of catastrophic failure. This limits the material's applicability in reliability-critical applications, as the impending failure is not evident. The material is also susceptible to metal fatigue with crack growth. A two-phase composite structure with amorphous matrix and a ductile dendritic crystalline-phase reinforcement, or a metal matrix composite reinforced with fibers of other material can reduce or eliminate this disadvantage.〔The case for bulk metallic glass, Materials Today, March 2004〕 抄文引用元・出典: フリー百科事典『 ウィキペディア（Wikipedia）』 ■ウィキペディアで「Liquidmetal」の詳細全文を読む スポンサード リンク
|