SiAlON ceramics are a specialist class of high-temperature refractory materials, with high strength (including at high temperature), good thermal shock resistance and exceptional resistance to wetting or corrosion by molten non-ferrous metals, compared to other refractory materials such as, for example, alumina. A typical use is with handling of molten aluminium. They also are exceptionally corrosion resistant and hence are also used in the chemical industry. Sialons also have high wear resistance, low thermal expansion and good oxidation resistance up to above ~1000 °C. They were invented by Kenneth Henderson Jack in 1984.
==Forms==
SiAlONs are ceramics based on the elements silicon (Si), aluminium (Al), oxygen (O) and nitrogen (N). They are solid solution of silicon nitride (Si3N4) and exist in three basic forms. Each form is iso-structural with one of the two common forms of silicon nitride, beta and alpha and with silicon oxynitride. The relationship between that of sialon and silicon nitride is similar to that between brass and pure copper. The later case, copper atoms are replaced by zinc to give a stronger alloy than the mother metal. In the case of sialon, there is substitution of silicon by aluminium with corresponding atomic replacement of nitrogen by oxygen, to satisfy valency requirements. The resulting 'solution' (sialon) has superior properties to the original pure solvent (silicon nitride).
抄文引用元・出典: フリー百科事典『 ウィキペディア（Wikipedia）』
■ウィキペディアで「Sialon」の詳細全文を読む
スポンサード リンク
| 翻訳と辞書 : 翻訳のためのインターネットリソース |
Copyright(C) kotoba.ne.jp 1997-2016. All Rights Reserved.
|
|